非显而易见性评估仅供参考，不构成法律建议。
权利要求列表点击可跳转
对比文件列表
| 编号 | 名称 |
|---|---|
| 0 | 2016-05-09_JP2016070215A_发明专利_JP2016070215A 減量弁の異常判定装置.docx |
| 0 | 2014-02-05_KR1020140013174A_发明公开_KR1020140013174A 탄소섬유 전구체용 폴리아크릴로나이트릴계 공중합체 및 이의 제조방법_+++A_G_K_e_f+++.docx |
| 0 | 2014-02-21_KR101365142B_发明授权_KR101365142B1 탄소섬유 전구체용 폴리아크릴로나이트릴계 공중합체 및 이의 제조방법_+++A_E_F_G_K_h+++.docx |
| 0 | 2014-03-27_JP2014054437A_发明专利_JP2014054437A Pachinko machine.docx |
| 0 | 2014-10-27_JP2014201728A_发明专利_JP2014201728A アクリロニトリル系共重合体粒子とその製造方法_+++D_a_b_f_i_k_l+++.docx |
| 0 | 2014-11-20_JP2014217371A_发明专利_JP2014217371A 伸餅用成形具及び伸餅の成形方法及び伸餅.docx |
| 0 | 2015-03-16_JP2015048378A_发明专利_JP2015048378A アクリロニトリル系重合体粒子及び製造方法_+++D+++.docx |
| 0 | 2015-04-29_CN104558394A_发明公开_CN104558394A 粘度可控的聚丙烯腈碳纤维纺丝原液的制备方法_+++A_E_F_G_H_d+++.docx |
| 0 | 2015-06-11_US2015158963A_发明申请_US20150158963A1 METHOD FOR PRODUCING (METH)ACRYLIC RESIN COMPOSITION_+++D+++.docx |
| 0 | 2015-06-17_CN104710565A_发明公开_CN104710565A 一种三元聚丙烯腈共聚物的制备方法_+++G_L_e_f_k+++.docx |
| 0 | 2015-08-13_KR1020150092603A_发明公开_KR1020150092603A 태양 전지 모듈.docx |
| 0 | 2016-02-24_JP5869997B_发明专利_JP5869997B2 パチンコ機.docx |
| 0 | 2013-11-28_JP2013237746A_发明专利_JP2013237746A Method for producing acrylonitrile-based polymer_+++D+++.docx |
| 0 | 2016-05-26_US2016145772A_发明申请_US20160145772A1 POLYACRYLONITRILE-BASED PRECURSOR FIBER FOR CARBON FIBER, AND PRODUCTION METHOD THEREFOR_+++A_G_K_L_f+++.docx |
| 0 | 2016-05-30_None_发明专利_JPWO2014002503A1 （メタ）アクリル樹脂組成物の製造方法_+++D+++.docx |
| 0 | 2016-09-23_JP2016169063A_发明专利_JP2016169063A 建設機械.docx |
| 0 | 2016-12-22_JP2016540131A_发明专利_JP2016540131A 炭素繊維用ポリアクリロニトリル系前駆体繊維及びその製造方法_+++A_G_f_k_l+++.docx |
| 0 | 2017-01-11_CN104710565B_发明授权_CN104710565B 一种三元聚丙烯腈共聚物的制备方法_+++G_H_e_f+++.docx |
| 0 | 2017-02-08_JP6075401B_发明专利_JP6075401B2 建設機械.docx |
| 0 | 2017-04-27_None_发明专利_JPWO2016021366A1 光学シンボルの読み取り装置および読み取り方法.docx |
| 0 | 2017-09-04_KR101774282B_发明授权_KR101774282B1 전자부품의 분배 장치.docx |
| 0 | 2017-09-20_JP6197775B_发明专利_JP6197775B2 減量弁の異常判定装置.docx |
| 0 | 2017-09-28_US2017275452A_发明申请_US20170275452A1 METHOD FOR PREPARING MODIFIED ACRYLONITRILE-BUTADIENE-STYRENE RESIN, AND MODIFIED ACRYLONITRILE-BUTADIENE-STYRENE RESIN PREPARED THEREBY.docx |
| 0 | WO2014002503A1_Description_20260621_2215_+++D+++.docx |
| 0 | 2007-07-19_JP2007182645A_发明专利_JP2007182645A Method for producing acrylic fiber_+++A_G_f+++.docx |
| 0 | 1986-02-20_KR1019860000807A_发明公开_KR1019860000807A 유자차의 제조 방법.docx |
| 0 | 1986-06-28_KR1019860000807B_发明授权_KR1019860000807B1 고분자량 아크릴로니트릴계 중합체의 제조법_+++D_E+++.docx |
| 0 | 1990-02-20_US4902762A_发明授权_US4902762A Process for preparing carbon fibers of high strength_+++A_E_F+++.docx |
| 0 | 1998-03-17_US5728793A_发明授权_US5728793A Process for production of methacrylate polymers_+++D+++.docx |
| 0 | 2003-03-05_JP2003064108A_发明专利_JP2003064108A Method for producing water-soluble polymer_+++D_E_K_L+++.docx |
| 0 | 2003-07-23_KR1020030062247A_发明公开_KR1020030062247A 에틸렌옥사이드계 공중합체의 제조방법_+++D_E+++.docx |
| 0 | 2003-08-21_US2003158374A_发明申请_US20030158374A1 Production process for ethylene oxide copolymer_+++D_e+++.docx |
| 0 | 2003-10-10_JP2003288317A_发明专利_JP2003288317A System and method for detecting and compensating for runt block data transfer.docx |
| 0 | 2004-03-12_KR1020040022397A_发明公开_KR1020040022397A 바운더리 스캔 장치.docx |
| 0 | 2006-05-04_KR100576274B_发明授权_KR100576274B1 바운더리 스캔 장치.docx |
| 0 | 2006-08-16_CN1820033A_发明公开_CN1820033A 用于碳纤维前体的聚合物.docx |
| 0 | 1984-12-17_KR1019840008658A_发明公开_KR1019840008658A 고분자량 아크릴로니트릴계 중합체의 제조법.docx |
| 0 | 2008-12-25_JP2008310786A_发明专利_JP2008310786A Treatment simulation system for cancer patient.docx |
| 0 | 2009-01-14_CN101343337A_发明公开_CN101343337A 一种制造碳纤维原丝用聚合物的聚合方法_+++E_L_a_d+++.docx |
| 0 | 2009-10-07_CN101553511A_发明公开_CN101553511A 聚丙烯腈类聚合物和其制造方法及碳纤维母体纤维的制造方法及碳纤维和其制造方法_+++A_E_F_G_H_K+++.docx |
| 0 | 2010-01-07_US2010003515A_发明申请_US20100003515A1 POLYACRYLONITRILE POLYMER, METHOD OF PRODUCING THE SAME, METHOD OF PRODUCING PRECURSOR FIBER USED FOR PRODUCING CARBON FIBER, CARBON FIBER AND METHOD OF P_+++A_F_G_H_K_e_l+++.docx |
| 0 | 2010-09-15_CN101343337B_发明授权_CN101343337B 一种制造碳纤维原丝用聚合物的聚合方法_+++K_L+++.docx |
| 0 | 2010-10-22_KR1020100113813A_发明公开_KR1020100113813A 탄소섬유용 아크릴로니트릴계 전구체 섬유 제조를 위한 용액중합 방법_+++A_E_F_G_K_L_d_h+++.docx |
| 0 | 2011-05-26_KR101037115B_发明授权_KR101037115B1 탄소섬유용 아크릴로니트릴계 전구체 섬유 제조를 위한 용액중합 방법_+++A_E_F_G_K_L_h+++.docx |
| 0 | 2011-06-24_KR1020110070773A_发明公开_KR1020110070773A 전자부품의 분배 장치.docx |
| 0 | 2012-01-11_CN101553511B_发明授权_CN101553511B 聚丙烯腈类聚合物和其制造方法及碳纤维母体纤维的制造方法及碳纤维和其制造方法_+++A_E_F_G_H_K_l+++.docx |
| 0 | 2012-10-22_JP2012201739A_发明专利_JP2012201739A Polyacrylonitrile polymer particle and method for producing the same_+++D_F+++.docx |
权利要求1
一种用于制备碳纤维的(甲基)丙烯腈类聚合物的制备方法，包括，将包含(甲基)丙烯腈类单体、选自(甲基)丙烯酸酯类单体和羧酸类单体中的一种或多种共聚单体、和反应溶剂的反应溶液添加到反应器中以进行溶液聚合；当所述反应器中的所述反应溶液的粘度为0.1泊以上且为250泊以下时，在所述反应器的能量消耗为1kW/m³至5kW/m³的条件下进行溶液聚合；以及当所述反应器中的所述反应溶液的粘度大于250泊且为450泊以下时，在所述反应器的能量消耗为8kW/m³至13kW/m³的条件下进行溶液聚合；其中，所述反应器的能量消耗是所述反应器中的搅拌器的能量消耗；其中，所述反应器是间歇型反应器；其中，相对于100重量份的所述(甲基)丙烯腈类单体，所述共聚单体以0.1重量份至10重量份被包含；其中，所述反应溶剂是选自二甲基亚砜、二甲基甲酰胺和二甲基乙酰胺中的一种或多种；其中，相对于100重量份的所述(甲基)丙烯腈类单体，所述反应溶剂以250重量份至500重量份被包含。
权利要求2
根据权利要求1所述的制备方法，其中，当所述反应器中的所述反应溶液的粘度为0.1泊以上且为250泊以下时，在所述反应器的能量消耗为2kW/m³至4kW/m³的条件下进行所述溶液聚合。
权利要求3
根据权利要求1所述的制备方法，其中，当所述反应器中的所述反应溶液的粘度大于250泊且为450泊以下时，在所述反应器的能量消耗为9kW/m³至11kW/m³的条件下进行所述溶液聚合。
权利要求4
根据权利要求1所述的制备方法，其中，所述溶液聚合在60℃至80℃下进行。
权利要求5
根据权利要求1所述的制备方法，其中，所述溶液聚合在65℃至75℃下进行。